Hvad bruges INCONEL til?

Inconel kemisk sammensætning

KARAKTER	ELEMENT (% EFTER MASSE)
KARAKTER	NI	CR	FE	MO	NB	CO	MN	CU	AL	TI	SI	C	S	P	B
600	72.0	14.0–17.0	6.0–10.0				1.0	0.5			0.5	0.15	0.015
617	44.2–56.0	20.0–24.0	3.0	8.0–10.0		10.0–15.0	0.5	0.5	0.8–1.5	0.6	0.5	0.15	0.015	0.015	0.006
625	58.0	20.0–23.0	5.0	8.0–10.0	3.15–4.15	1.0	0.5		0.4	0.4	0.5	0.1	0.015	0.015
690	59.5	30	9.2				0.35	0.01	0.02		0.35	0.019	0.003
718	50.0–55.0	17.0–21.0	saldo	2.8–3.3	4.75–5.5	1.0	0.35	0.2–0.8	0.65–1.15	0.3	0.35	0.08	0.015	0.015	0.006
X-750	70.0	14.0–17.0	5.0–9.0		0.7–1.2	1.0	1.0	0.5	0.4–1.0	2.25–2.75	0.5	0.08	0.01

Inconel Tilsvarende materiale

NORM	WERKSTOFF NR.	UNS	GOST	AFNOR	JIS	BS	DA	ELLER
Inconel 600	2.4816	N06600	МНЖМц 28-2,5-1,5	NC15FE11M	NCF 600	NA 13	NiCr15Fe	ЭИ868
Inconel 601	2.4851	N06601	XH60BT	NC23FeA	NCF 601	NA 49	NiCr23Fe	ЭИ868
Inconel 617	2.4663	N06617
Inconel 625	2.4856	N06625	ХН75МБТЮ	NC22DNB4M	NCF 625	NA 21	NiCr22Mo9Nb	ЭИ602
Inconel 690	2.4642	N06690
Inconel 718	2.4668	N07718
Inconel 725	-	N07725
Inconel X-750	2.4669	N07750

Inconel og Monel
Inconel og Monel er begge nikkelholdige legeringer. Men ud over at de indeholder nikkel som deres primære legeringsmiddel, indeholder de også andre grundstoffer som deres sekundære legeringsmidler. Monel, for eksempel, er sammensat af kobber, som udgør 30 til 40 procent af dens samlede vægt. Inconel indeholder chrom som dets hjælpelegeringsmiddel. Med hensyn til dets egenskaber er Monel en mellemtydende legering, mens Inconel er en højtydende type. Flere Inconel-legeringer er også kendt som superlegeringer, fordi de har fremragende korrosionsbestandighed og udkonkurrerer flere konventionelle legeringer ved høje temperaturer. Monel er et binært metal i solid opløsning, mens Inconel er en austenitisk højtemperaturlegering.

What is INCONEL used for

Inconel mekaniske egenskaber

	MASSEFYLDE	SMELTEPUNKT	STRÆK STYRKE	UDBYTTE STYRKE (0,2% OFFSET)	FORLÆNGELSE
600	8,47 g/cm3	1413 grader (2580 grader F)	Psi – 95,000 , MPa – 655	Psi – 45,000 , MPa – 310	40 %
601	8,1 g/cm3	1411 grader (2571 grader F)	Psi – 80,000 , MPa – 550	Psi – 30,000 , MPa – 205	30 %
617	8,3 g/cm³	1363 grader	Større end eller lig med 485 MPa	Større end eller lig med 275 MPa	25 %
625	8,4 g/cm3	1350 grader (2460 grader F)	Psi – 135,000 , MPa – 930	Psi – 75,000 , MPa – 517	42.5 %
690	8,3 g/cm³	1363 grader	Større end eller lig med 485 MPa	Større end eller lig med 275 MPa	25 %
718	8,2 g/cm3	1350 grader (2460 grader F)	Psi – 135,000 , MPa – 930	Psi – 70,000 , MPa – 482	45 %
725	8,31 g/cm3	1271 grader -1343 grader	1137 MPa	827 MPa	20 %
X-750	8,28 g/cm3	1430 grader	1267 MPa	868 MPa	25 %

Monel materialeækvivalent

NORM	WERKSTOFF NR.	UNS	GOST	AFNOR	JIS	BS	DA
Monel 400	2.4360	N04400	МНЖМц 28-2,5-1,5	NU-30M	NW 4400	NA 13	NiCu30Fe
Monel 404	2.4867	N04404
Monel 405		N04404
Monel K500	2.4375	N05500

Monel kemisk sammensætning

HANDELSNAVN	ASTM/AISI LEGERINGSTYPE	UNS	%CU	%AL	%TI	%FE	%MN	%SI	%NI
Monel 400	B 127, B 164	N04400	28-34			2,5 maks	2.0 maks	0.5 maks	63 min
Monel 401		N04401	28-34			2,5 maks	2.0 maks		63 min
Monel 404		N04404	Rem	0.05 maks		0.5 maks	0.1 maks	0.1 maks	52-57
Monel K-500	B 865	N05500	27-33	2.3-3.15	0.35-0.85	2.0 maks	1,5 maks	0.5 maks	63 min
Monel 405	B 164	N04405	28-34			2,5 maks	2.0 maks	0.5 maks	63 min

Monel mekaniske egenskaber

	MASSEFYLDE	SMELTEPUNKT	STRÆK STYRKE	UDBYTTE STYRKE (0,2% OFFSET)	FORLÆNGELSE
Monel 400	8,8 g/cm3	1350 grader (2460 grader F)	Psi – 80000, MPa – 550	Psi – 35000, MPa – 240	40 %
Monel 404	8,91 g/cm3	1300 - 1350 grad	70 KSI min (483 MPA min)	25 KSI min (172 MPA min)	35 %
Monel 405	8,80 g/cm3	1300 - 1350 grad	550 Mpa	240 Mpa	40 %
Monel K500	8,44 g/cm3	1350 grader (2460 grader F)	Psi – 160000, MPa – 1100	Psi – 115000, MPa – 790	20 %